| Productnaam: | U-bochtbuis | standaard: | ASTM A179, ASME SA179 |
|---|---|---|---|
| O.D.: | 6.35MM, 9.52MM, 12.7MM, 15.88MM, 19.05MM, 20MM, 22,23MM, 25MM, 25.4MM, 31.75MM, 38.1MM, 44.45MM, 50. | W.T.: | 0.89MM, 1MM, 1.24MM, 1.5MM, 1.65MM, 2MM, 2.11MM, 2.463MM, 2.5MM, 2.77MM, 3.05MM, 3.4MM |
| Lange: | 6000MM, 6096MM, S.R.L., DRL, DOUANE | NDT: | ET, UT, HT |
| Toepassing: | Boiler, Warmtewisselaar, Olie en Gasinstallatie, het Koelen, Condensator | ||
| Hoog licht: | api 5ct de buis van warmtewisselaaru,buis van u van de koolstof de naadloze warmtewisselaar,astm de buis van de warmtewisselaaru van a179 |
||
ASME SA179 warmtewisselaarbuis van koolstofarme staal naadloos U-buigbuis
ASTM A179/ASME SA179De buizen worden naadloos vervaardigd en koud getrokken. Meestal Deze systemen worden gebruikt in warmtewisselaars, olie- en gasinstallaties, chemische en petrochemische installaties, raffinaderijen, elektriciteitscentrales en hernieuwbare energiecentrales.Koelgetrokken naadloze buizen voor buisvormige warmtewisselaars, condensatoren en soortgelijke warmteoverdrachtapparaten.
Informatie dient te worden bevestigd:
1. Norm en naam van het materiaal: ASTM A179 / ASME SA 179 naadloze buizen.
2Vervaardiging uit koud getrokken produkten
3Hoeveelheid in meter, voet of stuk.
4- Grootte met inbegrip van de diameter en de minimumwanddikte
5. lengte per stuk (gevalsmatige of vaste lengte moet worden gespecificeerd)
A179 Chemische samenstelling:
|
C, %
|
Mn, %
|
P, %
|
S, %
|
|
0.06-0.18 |
0.27-0.63
|
0.035 max.
|
0.035 max.
|
A179 Mechanische eigenschappen:
|
Treksterkte, MPa
|
Kracht van de opbrengst, MPa
|
Verlenging, %
|
Hardheid, HRB
|
|
325 min.
|
180 min.
|
35 minuten.
|
Maximaal 72
|
A179 Buitenste diameter en tolerantie
| Buitentijdsdiameter, mm | Tolerantie mm |
| 3.2≤OD<25.4 | ±0.10 |
| 25.4≤OD≤38.1 | ±0.15 |
|
38.1 |
±0.20 |
| 50.8≤OD<63.5 | ±0.25 |
| 63.5≤OD<76.2 | ±0.30 |
| 76.2 | ±0.38 |
A179 Wanddikte & Tolerantie
| Buitenwijdte, mm | Tolerantie, % |
| 3.2≤OD<38.1 | +20/-0 |
| 38.1≤OD≤76.2 | +22/-0 |
| Standaard | staal | Trekkracht ((MPa) | Gewasopbrengst ((MPa) | Langwerpig ((%) | Verharding |
| 20MnG | 20MnG | ≥ 415 | ≥ 240 | ≥ 22 | |
| 25 miljoen euro | 25 miljoen euro | ≥ 485 | ≥ 275 | ≥ 20 | |
| 15CrMoG | 15CrMoG | 440 ¢ 640 | ≥235 | ≥ 21 | |
| 12Cr2MoG | 12Cr2MoG | 450 ¢ 600 | ≥ 280 | ≥ 20 | |
| 12Cr1MoVG | 12Cr1MoVG | 470 ¢ 640 | ≥ 255 | ≥ 21 | |
| 12Cr2MoWVTiB | 12Cr2MoWVTiB | 540 ¥735 | ≥ 345 | ≥ 18 | |
| 10Cr9Mo1VNb | 10Cr9Mo1VNb | ≥ 585 | ≥ 415 | ≥ 20 | |
| ASME SA210 | SA210A-1 | ≥ 415 | ≥ 255 | ≥ 30 | ≤143HB |
| SA210C | SA210C | ≥ 485 | ≥ 275 | ≥ 30 | ≤ 179HB |
| ASME SA213 | SA213 T11 | ≥ 415 | ≥205 | ≥ 30 | ≤ 163HB |
| SA213 T12 | SA213 T12 | ≥ 415 | ≥ 220 | ≥ 30 | ≤ 163HB |
| SA213 T22 | SA213 T22 | ≥ 415 | ≥205 | ≥ 30 | ≤ 163HB |
| SA213 T23 | SA213 T23 | ≥ 510 | ≥ 400 | ≥ 20 | ≤ 220HB |
| SA213 T91 | SA213 T91 | ≥ 585 | ≥ 415 | ≥ 20 | ≤ 250 HB |
| SA213 T92 | SA213 T92 | ≥ 620 | ≥440 | ≥ 20 | ≤ 250 HB |
| DIN17175 | ST45.8/III | 410 ¢530 | ≥ 255 | ≥ 21 | / |
| 15Mo3 | 15Mo3 | 450 ¢ 600 | ≥ 270 | ≥ 22 | |
| 13CrMo44 | 13CrMo44 | 440 ¢ 590 | ≥290 | ≥ 22 | |
| 10CrMo910 | 10CrMo910 | 480 ¢ 630 | ≥ 280 | ≥ 20 |
A179 zwart stalen buis minimaal koolstofgehalte is 0,06%. De naadloze stalen buis minimale treksterkte van 325MPa, opbrengststerkte van 180MPa. De minimale verlenging van A179 naadloze buis is 20%.
ASTM A179 (ASME SA179) koudgetrokken stalen buis
Dit is een effectieve manier van metaalcorrosie, het gebruik van de belangrijkste kenmerken zijn de volgende:
1. ASTM A179 fabrikanten van koudgetrokken naadloze buizen met een dikke dichte zinklaag bedekt met koudgetrokken naadloos buizenoppervlak,het kan koud getrokken naadloze buismatrix en elk contact met corrosieoplossing vermijden om de stalen matrix tegen corrosie te beschermenIn de algemene atmosfeer vormt het oppervlak van de zinklaag een laag dun en dicht zinkoxideoppervlak, het is moeilijk op te lossen in water, dus de staalmatrix speelt een beschermende rol.Als zinkoxide en andere componenten van de atmosfeer onoplosbaar zinkzout produceren, is het anti-corrosie effect wenselijker.
2Met ijzer-zinc legering laag, gecombineerd met dicht, en met de unieke anti-corrosie in de mariene atmosfeer en atmosferische atmosfeer.
3. ASTM A179 koud getrokken naadloze buis met een sterke slijtvastheid door de combinatie van vaste, zink-ijzer vermengbare stoffen.
4Aangezien zink een goede ductiliteit heeft, zijn de legeringslaag en de staalbasis aan een vaste stof bevestigd, zodat warmgewalste onderdelen koud, gewalst, getekend, gebogen en andere vormen kunnen worden zonder schade aan de coating.
5. warm gegalvaniseerde structuurstaalpijp, het equivalent van een gloeibehandeling, kan de mechanische eigenschappen van de staalmatrix effectief verbeteren om de lasspanning bij het vormen van staal te elimineren,is bevorderlijk voor het draaien van de staalconstructie.
6Het oppervlak van koud getrokken naadloze pijp na warm gegalvaniseerd is helder en mooi.